| General purpose acrylic AB glue | GB/T 7124 | Tensile shear strength: 15 – 22 MPa (for steel and aluminum) | Temperature range: -40°C to +120°C (up to 150°C for short periods) | Mixing ratio: 1:1 (by volume or weight) | Operating time: 3 – 8 minutes (25°C) |
| ASTM D1002 | Tensile strength: 20 – 30 MPa | Resistance to damp heat aging: After 500 hours at 85°C/85% RH, strength retention > 80%. | VOC content: Extremely low | Initial curing time: 10 – 20 minutes (25°C) |
| Elongation at break: 10% – 30% | Impact resistance and fatigue resistance: Good | Irritating odor: Yes, it should be used in a well-ventilated area. | Reach usable intensity: 30-60 minutes |
| Shore hardness: 75 – 85 Shore D | | | Application method: Two-component static mixing tube or independent coating |
| Transparent acrylic AB glue | ASTM D1003 | Light transmittance: ≥ 90% (after curing, comparable to plexiglass/PMMA) | UV resistance: Excellent; minimal yellowing and high transparency retention after QUV testing. | Mixing ratio: 1:1 | Operation time: 5 – 10 minutes |
| GB/T 7124, ASTM D1002 | Haze: ≤ 1% | Temperature range: -40°C to +110°C | Environmental certification: RoHS certified | Initial setting time: 15-25 minutes |
| Tensile shear strength: 12 – 18 MPa (for glass and transparent plastics) | Water resistance: Excellent; transparency and strength remain unchanged after long-term immersion in water. | Odor: Has a pungent odor | Key process: Extremely high cleanliness requirements; even the smallest impurities can affect the appearance. |
| Yellowing index (ΔYI): < 2 (after UV aging) | | | Application areas: Crystal handicrafts, glass furniture, display screen assembly, transparent signage |
| High-performance acrylic structural adhesives | GB/T 7124 | Tensile shear strength: 25 – 35 MPa (for steel and aluminum) | Temperature range: -40°C to 130°C | Mixing ratio: May be non-1:1 (e.g., 10:1) | Operation time: 2 – 5 minutes (fast response type) |
| ISO 11339 | T-Peel strength: 40 – 70 N/cm (demonstrating high toughness) | Fatigue resistance: Excellent, capable of withstanding dynamic loads. | VOC: Extremely low | Initial setting time: 5-15 minutes |
| Impact strength: Extremely high | Salt spray resistance, fuel oil resistance, and hydraulic oil resistance: Excellent performance. | Surface tolerance: Has a certain tolerance to oil-coated steel plates. | Construction method: A two-component metering and mixing device is required. |
| Shore hardness: 80 – 90 Shore D | | | Applicable substrates: metals, composite materials, engineering plastics (PP/PE requires pretreatment). |